ROBOFIL B 700
| ASME IIC SFA 5.29 / AWS A 5.29 | E110T5-K4MH4 |
| EN ISO 18276-A | T 69 5 Mn2NiCrMo B M 3 H5 |
| EN ISO 18276-B | T765T5-0MA-N4M2-UH5 |
| ASME IX Qualification | QW-432 F-N° 6 QW-442 A-N° 12 |
•Seamless high fill copper coated basic cored tubular wire for semi-automatic gas shielded arc welding
• Single and multipass welding of high strength steels
• Combines advantages of both seamless and seamed tubular wires
• Deposits have very lox hydrogen contents. HDM guaranteed < 4 ml/ 100g deposited metal on the whole parameter box
• No moisture pick up, excellent wire feeding properties
• Excellent mechanical properties
Robofil B 700 is a basic flux cored wire with high ductility and cracking resistance for high strength fine grained constructional steels. Tough at ambient temperatures and subzero temperatures, down to -50°C.
Examples
High strength steels | S500QL – S690QL
N-A-Xtra70, Weldox 700, HY80, HY100
T1, Superelso 700, Suprafort 700, Shoralsim 690
ISO/TR 15608: Groups 1.2, 1.3, 2.2 and 3.1 |
| TYPICAL ALL-WELD METAL ANALYSIS |
|---|
| C | Mn | Si | Cr | Ni | Mo | S | P |
|---|
| 0.05 | 1.40 | 0.40 | 0.50 | 2.40 | 0.50 | 0.015 | 0.005 |
| MINIMUM ALL-WELD METAL MECHANICAL PROPERTIES |
|---|
| Rm [MPa] | Rp 0.2% | A5[%] | KV[J] |
|---|
| 770 | 690 | 16 | 47 at -51°C |
| TYPICAL ALL-WELD MECHANICAL ANALYSIS |
|---|
| Rm [MPa] | Rp 0.2% | A5[%] | KV[J] |
|---|
| 900 | 840 | 20 | 60 at -51°C |
M21 (Ar + 15 - 25% CO2) gas mixtures according to EN ISO 14175
| Diameter [mm] | Current type | Current I [A] | Voltage [V] | Stick out [mm] |
|---|
| 1.2 | DC(+) or pulsed | 100 - 340 | 16 - 34 | 12 - 25 |
| 1.6 | DC(+) or pulsed | 160 - 470 | 20 - 36
| 15 - 25 |
EN ISO 6947: PA, PB
ASME IX: 1G, 1F, 2F
| Diameter | 1.2 mm | 1.6 mm |
|---|
| EN ISO 544 – ASME II C SFA-5.2 M |
| Spool type | BS300 |
| Weight | 15 kg |
Other packaging: please consult us